16 mm / C2 – Schütz Dental GmbH

Tizian Blank MT E 98 mm

Sat, 28 Feb 2026 15:03:45 +0000

Tizian Blank MT + 98 mm

Sat, 28 Feb 2026 15:03:23 +0000

“

with graduated light transmission

translucence of 49 % to 45 %

Special features:
Following the trend, a blank that combines the positive properties of the already established zirconium oxide qualities 4Y-TZP and the highly translucent 5Y-TZP in the enamel and in the body.

Suitable for: highly esthetic monolithic, fully anatomic crowns, partial crowns and bridges with up to 14 units, inlays, onlays, veneers and abutments. Due to its high esthetics, it is particularly suitable for the anterior and visible tooth area. All processing techniques are possible: Staining, cut-back and veneering techniques are possible.

The combination of 4Y (Extra Translucent with high strength) and 5Y (High Translucent with high translucency) results in improvements in the esthetic effect and safety for an unrestricted indication range of restorations. In addition to a smooth transition between the layers within the blank or restoration, we were able to achieve improved esthetics in relation to the Vita Classical Shade Guide.

Graduated strength

The smooth transition between the layers results in a graduated strength within the blank or restoration. This makes Tizian Blank MT + suitable for almost all indications.

Material

Zirconium dioxide type II, class 5 according to DIN EN ISO 6872
Flexural strength: typical mean value ? 1,100 MPa
Translucence graduation of &lt

priti®multidisc ZrO2 Multi Translucent 98 x 16 mm, Colour A1

Sat, 28 Feb 2026 15:01:49 +0000

Aesthetics and durability combined to create a true multi-talent.
The wonderful result of a merger between stability and natural beauty.

Our new multi-talent is the ideal product to support you along your individual path to highly aesthetic and durable dental restorations. This blank follows the trend to combine the positive features of the already established zirconium quality of 3Y-TZP and the highly translucent 5Y-TZP.

Just imagine mixing two different material classes…

What could result from it is a unique raw material combination of a high-strength and highly translucent ZrO₂.

We just did it! When adding our new and innovative TILLY philosophy, the result was a multi-talented product which defines a completely new generation!

Produce individual restorations for the anterior and posterior sector on natural tooth stumps and implants with priti®multidisc ZrO₂ Multi Translucent.
The special feature: graduation of shade and translucency with a simultaneous high flexural strength. These characteristics make priti®multidisc ZrO₂ Multi Translucent an extraordinary and flexible choice for a wide range of indications.

Benefits

Excellent dental aesthetics
Naturally graduated shade and translucency
High stability: flexural strength &gt, 1,100 MPa (typical average)
All processing techniques: painting technique, cut-back technique, veneering technique
Quick sintering, complete processing time ca. 4 hours, released for up to 3 unit restorations
High translucency in the incisal sector (&gt, 49 %), mechanical load capacity in the dentin sector

Which is technique is your favorite?
Select from these techniques: painting technique, cut-back technique, veneering technique.

Indications:

Individual restorations for the anterior and posterior sector on natural tooth stumps and implants
Highly aesthetic monolithic fully anatomic crowns, partial crowns and bridges of up to 14 units
Inlays, onlays, veneers and abutments
Quick sintering of restorations with up to 3 units

Facts:

Zirkonium dioxide type II, class 5 accordingt to DIN EN ISO 6872
Flexural strength: typical average ? 1,100 MPa
Translucency graduation of &lt, 40 % to &gt, 49 %
Thin wall thickness, in the anterior sector 0.4 mm and in the posterior sector 0.6 mm for individual crowns
Precise margins and edges due to high density material
Can be veneered with all ceramics which are adapted to the CTE of 10 · 10^-6 · K^-1 von ZrO₂
Color stability across the batches
Homogeneous coloration
Reproducible colors
Biocompatible

priti®multidisc ZrO2 Translucent, 98 mm

Sat, 28 Feb 2026 15:00:00 +0000

Available in 16 VITA shades and in white, with a translucency of 40 %.

Indications:

Very aesthetic monolithic, fully anatomical crowns, partial crowns and bridges with up to 16-units, frameworks
Highly recommended for partially or fully veneered aesthetic work

Advantages of monochromatic precolored blanks

Why use precolored material? Applying a penetrating, homogeneous stain to the material does away with the need for processes such as dipping, painting and drying. This does not only save time and effort, but it also helps to avoid potential manual errors during the staining process. This reduces production costs and your customers will appreciate the consistent and reproducible color quality. Since the material comes fully precolored, even finishing or adjustment grinding do not leave light spots, which would have a negative effect on the appearance of the finished product.

Industrially precolored zirconium blanks are reproducible. Precolored material is gentle on your sintering furnace and protects its components from damage. Acid-based liquid stains can emit fumes during the sintering process which leave deposits on the the heating elements of the furnace and contaminate them. This can cause undesirable discoloration and/or loss of translucency. Using industrially precolored zirconium ensures consistent color results.

Suitable for:

open milling system with a blank holder for round blanks with a diameter of 98.5 mm

Material:

Zirconium type II, class 5 according to DIN EN ISO 6872
Good flexural strength of &gt, 1,100 MPa
High translucency of 40 %
High aesthetics
Very good resistance to aging
Thin wall thicknesses for single crowns in the anterior tooth area 0.4 mm and in the posterior tooth area 0.6 mm
Biocompatible