FuturaJet powder pink-opaque, pink opaque, 1000 g
Advantages
- Wide choice of colors
- Easy to use
- Universally applicable
Properties
- Injection technique
- Full dentures
- Completing frameworks
- Denture relinings
- Repairs
Description
Self-curing prosthesis acrylic that covers practically all indications. Flow technique, injection technique.and many more.
Product number:
650022
Questions about the product? We are glad to be here for you!
Product information "FuturaJet powder pink-opaque, pink opaque, 1000 g"
FuturaJet is the multi-talent in the acrylics world. It is eminently suitable for the injection method and all conventional acrylics techniques.
Your benefits:
- Wide choice of colors
- Easy to use
- Universally applicable
- Excellent mechanical properties
- Extraordinary fit
Polymerization:
- Flask temperature 35 °C (95 °F), injection pressure 30 min.
- Polymerization time: 15 min. at 2-4 bar, water temperature 45 °C (113 °F).
Mixing ratio powder:liquid (weight [g]):
- 2:1 (free dosage)
Processing time:
- 4.5 min.
Physical properties:
- Vickers hardness: ca. 140 MPa
- Flexural strength: ca. 95 MPa
- E-module: ca. 2,700 MPa
- Water absorption: 23.3 µg/mm³
- Water solubility: 1.1 µg/mm³
- Residual monomer: complies with the standard
12 kg containers upon request.
FuturaJet liquid is available in 0.5 l or 1 l containers.
| Powder/Liquid: | Pulver |
|---|---|
| Processing: | Kaltpolymerisat |
Cutsomers also bought
FuturaJet liquid, 1000 ml,
Monomer liquid for your FuturaJet acrylic. FuturaJet is the multi-talent in the acrylics world. It is eminently suitable for the injection method and all conventional acrylics techniques. Your benefits: Wide choice of colors Easy to use Universally applicable Excellent mechanical properties Extraordinary fit Polymerization: Flask temperature 35 °C (95 °F), injection pressure 30 min. Polymerization time: 15 min. at 2-4 bar, water temperature 45 °C (113 °F). Mixing ratio powder:liquid (weight [g]): 2:1 (free dosage) Processing time: 4.5 min. Physical properties: Vickers hardness: ca. 140 MPa Flexural strength: ca. 95 MPa E-module: ca. 2,700 MPa Water absorption: 23.3 µg/mm³ Water solubility: 1.1 µg/mm³ Residual monomer: complies with the standard Availability of FuturaJet powder: 500 g or 1 kg container.
FuturaJet powder, pink, pink, 1000 g
FuturaJet is the multi-talent in the acrylics world. It is eminently suitable for the injection method and all conventional acrylics techniques. Your benefits: Wide choice of colors Easy to use Universally applicable Excellent mechanical properties Extraordinary fit Polymerization: Flask temperature 35 °C (95 °F), injection pressure 30 min. Polymerization time: 15 min. at 2-4 bar, water temperature 45 °C (113 °F). Mixing ratio powder:liquid (weight [g]): 2:1 (free dosage) Processing time: 4.5 min. Physical properties: Vickers hardness: ca. 140 MPa Flexural strength: ca. 95 MPa E-module: ca. 2,700 MPa Water absorption: 23.3 µg/mm³ Water solubility: 1.1 µg/mm³ Residual monomer: complies with the standard 12 kg containers upon request.FuturaJet liquid is available in 0.5 l or 1 l containers.
Tizian Blank NEM fine 98 mm
Tizian Blanks NEM (non-precious metal) are made of beryllium-free and cadmium-free CoCr ceramic alloy according to DIN EN OSP 22674 and EN ISO 9693 for applications with thin cross-sections which are exposed to extreme forces. Examples are removable partial dentures, clasps, thin veneered individual crowns, fixed full arch dentures or bridges with small cross-sections, bars, fixations, implant-supported supraconstructions. Properties: Alloy type: 4Density: 8.8 g/cm³Vickers hardness: 285 HV 10/30CTE- value (25-500 °C): 14,4*10-6 K-1Oxidation without vacuum (Point 4c): 1000 °CMass content of the components (in weight-%)*: Co 63, Cr 29, Mo 6 / Mn x, Nb x, Si x, Fe xTensile strength: 680 MPa0.2 % yield point: 400 MPaElongation at break: 9 %E-module: 250 GPa *X= <, 1%
Tizian Blank NEM fine 98 mm
Tizian Blanks NEM (non-precious metal) are made of beryllium-free and cadmium-free CoCr ceramic alloy according to DIN EN OSP 22674 and EN ISO 9693 for applications with thin cross-sections which are exposed to extreme forces. Examples are removable partial dentures, clasps, thin veneered individual crowns, fixed full arch dentures or bridges with small cross-sections, bars, fixations, implant-supported supraconstructions. Properties: Alloy type: 4Density: 8.8 g/cm³Vickers hardness: 285 HV 10/30CTE- value (25-500 °C): 14,4*10-6 K-1Oxidation without vacuum (Point 4c): 1000 °CMass content of the components (in weight-%)*: Co 63, Cr 29, Mo 6 / Mn x, Nb x, Si x, Fe xTensile strength: 680 MPa0.2 % yield point: 400 MPaElongation at break: 9 %E-module: 250 GPa *X= <, 1%
T11 Tizian Cut 5/3.5 PMMA finemilling single point mill, 2,5 mm, 6 mm shaft
Radius cutter single-edged, edge Ø 2.5 mm, shaft Ø 6 mm, total length 53 mm, max. blank height = 25 mm. Processing type: pilot milling Blank material: PMMA, PEEK Coating type: uncoated Ring color: gold For milling machines: Tizian Cut 5.2, Tizian Cut 5.2 plus, Tizian Cut 5 option metal milling (6 mm shaft), CORiTEC 550i, CORiTEC 750i
T4/T9 Tizian Cut 5/3.5 Metal Drill CoCr/Ti 1mm, 6 mm shaft
Radius cutter short, double-edged, edge Ø 1 mm, shaft Ø 6 mm, total length 45 mm. Max. blank height = short up to 15 mm, long up to 20 mm. Processing type: fine finishing Blank material: CoCr, titanium Type: coated Coding color: gold For the milling machines: Tizian Cut 5.2, Tizian Cut 5.2 plus, Tizian Cut 5 option metal milling (6 mm shaft), CORiTEC 550i, CORiTEC 750i