priti®multidisc ZrO2 Multi Translucent 98 x 16 mm, Colour A3

Aesthetics and durability combined to create a true multi-talent. The wonderful result of a merger between stability and natural beauty.Our new multi-talent is the ideal product to support you along your individual path to highly aesthetic and durable dental restorations. This blank follows the trend to combine the positive features of the already established zirconium quality of 3Y-TZP and the highly translucent 5Y-TZP. Just imagine mixing two different material classes... What could result from it is a unique raw material combination of a high-strength and highly translucent ZrO2. We just did it! When adding our new and innovative TILLY philosophy, the result was a multi-talented product which defines a completely new generation! Produce individual restorations for the anterior and posterior sector on natural tooth stumps and implants with priti®multidisc ZrO2 Multi Translucent.The special feature: graduation of shade and translucency with a simultaneous high flexural strength. These characteristics make priti®multidisc ZrO2 Multi Translucent an extraordinary and flexible choice for a wide range of indications.Benefits Excellent dental aesthetics Naturally graduated shade and translucency High stability: flexural strength >, 1,100 MPa (typical average) All processing techniques: painting technique, cut-back technique, veneering technique Quick sintering, complete processing time ca. 4 hours, released for up to 3 unit restorations High translucency in the incisal sector (>, 49 %), mechanical load capacity in the dentin sector Which is technique is your favorite?Select from these techniques: painting technique, cut-back technique, veneering technique. Indications: Individual restorations for the anterior and posterior sector on natural tooth stumps and implants  Highly aesthetic monolithic fully anatomic crowns, partial crowns and bridges of up to 14 units Inlays, onlays, veneers and abutments Quick sintering of restorations with up to 3 units Facts: Zirkonium dioxide type II, class 5 accordingt to DIN EN ISO 6872 Flexural strength: typical average ? 1,100 MPa Translucency graduation of <, 40 % to >, 49 % Thin wall thickness, in the anterior sector 0.4 mm and in the posterior sector 0.6 mm for individual crowns Precise margins and edges due to high density material Can be veneered with all ceramics which are adapted to the CTE of 10 · 10-6 · K-1 von ZrO2  Color stability across the batches Homogeneous coloration Reproducible colors Biocompatible  

Aesthetics and durability combined to create a true multi-talent. The wonderful result of a merger between stability and natural beauty.Our new multi-talent is the ideal product to support you along your individual path to highly aesthetic and durable dental restorations. This blank follows the trend to combine the positive features of the already established zirconium quality of 3Y-TZP and the highly translucent 5Y-TZP. Just imagine mixing two different material classes... What could result from it is a unique raw material combination of a high-strength and highly translucent ZrO2. We just did it! When adding our new and innovative TILLY philosophy, the result was a multi-talented product which defines a completely new generation! Produce individual restorations for the anterior and posterior sector on natural tooth stumps and implants with priti®multidisc ZrO2 Multi Translucent.The special feature: graduation of shade and translucency with a simultaneous high flexural strength. These characteristics make priti®multidisc ZrO2 Multi Translucent an extraordinary and flexible choice for a wide range of indications.Benefits Excellent dental aesthetics Naturally graduated shade and translucency High stability: flexural strength >, 1,100 MPa (typical average) All processing techniques: painting technique, cut-back technique, veneering technique Quick sintering, complete processing time ca. 4 hours, released for up to 3 unit restorations High translucency in the incisal sector (>, 49 %), mechanical load capacity in the dentin sector Which is technique is your favorite?Select from these techniques: painting technique, cut-back technique, veneering technique. Indications: Individual restorations for the anterior and posterior sector on natural tooth stumps and implants  Highly aesthetic monolithic fully anatomic crowns, partial crowns and bridges of up to 14 units Inlays, onlays, veneers and abutments Quick sintering of restorations with up to 3 units Facts: Zirkonium dioxide type II, class 5 accordingt to DIN EN ISO 6872 Flexural strength: typical average ? 1,100 MPa Translucency graduation of <, 40 % to >, 49 % Thin wall thickness, in the anterior sector 0.4 mm and in the posterior sector 0.6 mm for individual crowns Precise margins and edges due to high density material Can be veneered with all ceramics which are adapted to the CTE of 10 · 10-6 · K-1 von ZrO2  Color stability across the batches Homogeneous coloration Reproducible colors Biocompatible  

Tizian Blanks NEM (non-precious metal) are made of beryllium-free and cadmium-free CoCr ceramic alloy according to DIN EN OSP 22674 and EN ISO 9693 for applications with thin cross-sections which are exposed to extreme forces. Examples are removable partial dentures, clasps, thin veneered individual crowns, fixed full arch dentures or bridges with small cross-sections, bars, fixations, implant-supported supraconstructions. Properties: Alloy type: 4Density: 8.8 g/cm³Vickers hardness: 285 HV 10/30CTE- value (25-500 °C): 14,4*10-6 K-1Oxidation without vacuum (Point 4c): 1000 °CMass content of the components (in weight-%)*: Co 63, Cr 29, Mo 6 / Mn x, Nb x, Si x, Fe xTensile strength: 680 MPa0.2 % yield point: 400 MPaElongation at break: 9 %E-module: 250 GPa *X= <, 1%

Tizian Blanks NEM (non-precious metal) are made of beryllium-free and cadmium-free CoCr ceramic alloy according to DIN EN OSP 22674 and EN ISO 9693 for applications with thin cross-sections which are exposed to extreme forces. Examples are removable partial dentures, clasps, thin veneered individual crowns, fixed full arch dentures or bridges with small cross-sections, bars, fixations, implant-supported supraconstructions. Properties: Alloy type: 4Density: 8.8 g/cm³Vickers hardness: 285 HV 10/30CTE- value (25-500 °C): 14,4*10-6 K-1Oxidation without vacuum (Point 4c): 1000 °CMass content of the components (in weight-%)*: Co 63, Cr 29, Mo 6 / Mn x, Nb x, Si x, Fe xTensile strength: 680 MPa0.2 % yield point: 400 MPaElongation at break: 9 %E-module: 250 GPa *X= <, 1%

Ball-end mill, double-edged, edge Ø 1.5 mm, shaft Ø 6 mm, total length 48 mm Processing type: drilling a screw channel Blank material: CoCr, titanium Type: coated Coding color: gold For the milling machines: Tizian Cut 5.2, Tizian Cut 5.2 plus, Tizian Cut 5 option metal milling (6 mm shaft), CORiTEC 550i, CORiTEC 750i

Radius cutter short, double-edged, edge Ø 2 mm, shaft Ø 6 mm, total length 45 mm. Max. blank height = short up to 15 mm, long up to 20 mm. Processing type: roughing Blank material: CoCr, titanium Type: coated Coding color: gold For the milling machines: Tizian Cut 5.2, Tizian Cut 5.2 plus, Tizian Cut 5 option metal milling (6 mm shaft), CORiTEC 550i, CORiTEC 750i