priti®multidisc ZrO2 Opaque, 98x 14, Colour A3

Used for the fabrication of temporary crowns and bridges to replace teeth or groups of teeth. Use in all open CAD-CAM systems   Your benefits: Very high material homogeneity due to the industrial polymerization process. Balanced combination of breaking strength and elasticity for clinical use. This guarantees excellent long-term stability. Excellent abrasion resistance. Ensures high process reliability, no mixing errors, no polymerization shrinkage and no unpleasant odour, as no hand mixing or cartridge. Extended milling properties thanks to economical production. Long-lasting color stability and aesthetics. Natural fluorescence.

With a translucency of 35 %.Indications:   Very aesthetic monolithic, fully anatomical crowns, partial crowns and bridges with up to 16-units, frameworks     Recommended for covering discolored tooth stumps or metal structures Advantages of monochromatic precolored blanks Why use precolored material? Applying a penetrating, homogeneous stain to the material does away with the need for processes such as dipping, painting and drying. This does not only save time and effort, but it also helps to avoid potential manual errors during the staining process. This reduces production costs and your customers will appreciate the consistent and reproducible color quality. Since the material comes fully precolored, even finishing or adjustment grinding do not leave light spots, which would have a negative effect on the appearance of the finished product. Industrially precolored zirconium blanks are reproducible. Precolored material is gentle on your sintering furnace and protects its components from damage. Acid-based liquid stains can emit fumes during the sintering process which leave deposits on the the heating elements of the furnace and contaminate them. This can cause undesirable discoloration and/or loss of translucency. Using industrially precolored zirconium ensures consistent color results. Suitable for: open milling system with a blank holder for round blanks with a diameter of 98.5 mm Material:   Zirconium type II, class 5 according to DIN EN ISO 6872   Good flexural strength of >, 1,150 MPa   Very high translucency of 35 % Good aging resistance Thin wall thicknesses for single crowns in the anterior tooth area 0.4 mm and in the posterior tooth area 0.6 mm   Biocompatible    

With a translucency of 35 %.Indications:   Very aesthetic monolithic, fully anatomical crowns, partial crowns and bridges with up to 16-units, frameworks     Recommended for covering discolored tooth stumps or metal structures Advantages of monochromatic precolored blanks Why use precolored material? Applying a penetrating, homogeneous stain to the material does away with the need for processes such as dipping, painting and drying. This does not only save time and effort, but it also helps to avoid potential manual errors during the staining process. This reduces production costs and your customers will appreciate the consistent and reproducible color quality. Since the material comes fully precolored, even finishing or adjustment grinding do not leave light spots, which would have a negative effect on the appearance of the finished product. Industrially precolored zirconium blanks are reproducible. Precolored material is gentle on your sintering furnace and protects its components from damage. Acid-based liquid stains can emit fumes during the sintering process which leave deposits on the the heating elements of the furnace and contaminate them. This can cause undesirable discoloration and/or loss of translucency. Using industrially precolored zirconium ensures consistent color results. Suitable for: open milling system with a blank holder for round blanks with a diameter of 98.5 mm Material:   Zirconium type II, class 5 according to DIN EN ISO 6872   Good flexural strength of >, 1,150 MPa   Very high translucency of 35 % Good aging resistance Thin wall thicknesses for single crowns in the anterior tooth area 0.4 mm and in the posterior tooth area 0.6 mm   Biocompatible    

With a translucency of 35 %.Indications:   Very aesthetic monolithic, fully anatomical crowns, partial crowns and bridges with up to 16-units, frameworks     Recommended for covering discolored tooth stumps or metal structures Advantages of monochromatic precolored blanks Why use precolored material? Applying a penetrating, homogeneous stain to the material does away with the need for processes such as dipping, painting and drying. This does not only save time and effort, but it also helps to avoid potential manual errors during the staining process. This reduces production costs and your customers will appreciate the consistent and reproducible color quality. Since the material comes fully precolored, even finishing or adjustment grinding do not leave light spots, which would have a negative effect on the appearance of the finished product. Industrially precolored zirconium blanks are reproducible. Precolored material is gentle on your sintering furnace and protects its components from damage. Acid-based liquid stains can emit fumes during the sintering process which leave deposits on the the heating elements of the furnace and contaminate them. This can cause undesirable discoloration and/or loss of translucency. Using industrially precolored zirconium ensures consistent color results. Suitable for: open milling system with a blank holder for round blanks with a diameter of 98.5 mm Material:   Zirconium type II, class 5 according to DIN EN ISO 6872   Good flexural strength of >, 1,150 MPa   Very high translucency of 35 % Good aging resistance Thin wall thicknesses for single crowns in the anterior tooth area 0.4 mm and in the posterior tooth area 0.6 mm   Biocompatible    

T86/T96 - Radius cutter Diameter: Ø 1 mmBlade: double-edgedShaft: Ø 6 mmTotal length: 45 mmBlank material: CoCr, titaniumCoating type: coatedFor milling systems: Tizian 3.5 Series, Tizian Cut 5.2 Pro, Tizian Cut 5.2 Pro Plus, Tizian Cut 5.2, Tizian Cut 5.2 plus, Tizian Cut 5, CORiTEC 550i, CORiTEC 650i

Tizian Blanks NEM are made from a biocompatible non-precious alloy on CoCr basis. The blanks are free of nickel and beryllium. Mill your crowns and bridges from Tizian Blanks NEM. Specifically well suited bonding oxide formers ensure an optimal metal ceramic bond. Its Vickers hardness of 320 HV10 makes the CoCr material easy to mill and to polish. Indcations: Crowns and bridges to be veneered with ceramics Inlays and onlays Abutments Special restorations such as cantilever bridges or attachment parts: responsibility of the attending dentist (evaluation ot the responsibility) Your benefits: Homogenous quality Excellent surface quality Ideal Vickers hardness (275 HV10) Free of molybdenum for a smooth for a smooth movement of the telescopic crowns Clean material removal for a long service-life of the mills Stable...