priti®multidisc ZrO2 multicolor High Translucent, 98x 14, Colour A light

Material:	Zirkoniumdioxid
Shape:	98mm rund

priti®multidisc ZrO2 multicolor High Translucent, 98x 20, Colour A light

Cubic zirconium, with a translucency of 49 %. Indications: Highly aesthetic monolithic, fully anatomical crowns, partial crowns and bridges with up to 3-units, inlays, onlays and veneers Highly recommended for partially or fully veneered highly aesthetic work Your benefits: highly aesthetic quick easy reproducible Suitable for: open milling system with a blank holder for round blanks with a diameter of 98.5 mm Material: Zirconium type II, class 4 according to DIN EN ISO 6872 Good flexural strength of >, 650 MPa Very high translucency of 49 %, comparable with lithium disilicate Superior aesthetics Very good resistance to aging Thin wall thicknesses for single crowns in the anterior tooth area 0.4 mm and in the posterior tooth area 0.6 mm Biocompatible

Tizian Blank MT + 98 mm

"with graduated light transmission translucence of 49 % to 45 % Special features:Following the trend, a blank that combines the positive properties of the already established zirconium oxide qualities 4Y-TZP and the highly translucent 5Y-TZP in the enamel and in the body. Suitable for: highly esthetic monolithic, fully anatomic crowns, partial crowns and bridges with up to 14 units, inlays, onlays, veneers and abutments. Due to its high esthetics, it is particularly suitable for the anterior and visible tooth area. All processing techniques are possible: Staining, cut-back and veneering techniques are possible. The combination of 4Y (Extra Translucent with high strength) and 5Y (High Translucent with high translucency) results in improvements in the esthetic effect and safety for an unrestricted indication range of restorations. In addition to a smooth transition between the layers within the blank or restoration, we were able to achieve improved esthetics in relation to the Vita Classical Shade Guide. Graduated strength The smooth transition between the layers results in a graduated strength within the blank or restoration. This makes Tizian Blank MT + suitable for almost all indications. Material Zirconium dioxide type II, class 5 according to DIN EN ISO 6872 Flexural strength: typical mean value ? 1,100 MPa Translucence graduation of <

priti®multidisc ZrO2 multicolor Extra Translucent, 98 x 18, Color A light

There is a new zirconium dioxide for everyone!priti®multidisc ZrO? multicolor Extra Translucent with a translucence of 45 % and flexural strength >, 1,150 MPa. A cleverly devised zirconium dioxide concept which is an outstanding choice for almost every user. It makes working matchlessly easy. Beautiful &, strong! Real aesthetics - one fits all! Indications: priti®multidisc ZrO? Extra Translucent are excellently suited to the production of monolithic fully anatomic and partially or fully veneered crowns and bridges with up to 16 units individual abutments for anterior and side teeth on abutment teeth and implants What makes this product so special is its well-balanced relationship between high transparency and flexural strength. This indicates it for an especially wide range of indications.Material: Zirconium dioxide type II, class 5 according to DIN EN ISO 6872 Flexural strength >, 1,150 MPa Exceptional transparency of 45 % Thin wall thickness in the anterior tooth range of 0.4 mm and in the side tooth range of 0.6 mm for individual crowns Precise margins and edges because of a highly condensed material Can be veneered with close to every commercially available ceramic material which is adjusted to the CTE 10 · 10-6 K-1 of ZrO? Batch-independent color accuracy Homogeneous colorization Reproducible colors Biocompatible

priti®multidisc ZrO2 multicolor Extra Translucent, 98 x 14, Color A light

There is a new zirconium dioxide for everyone!priti®multidisc ZrO? multicolor Extra Translucent with a translucence of 45 % and flexural strength >, 1,150 MPa. A cleverly devised zirconium dioxide concept which is an outstanding choice for almost every user. It makes working matchlessly easy. Beautiful &, strong! Real aesthetics - one fits all! Indications: priti®multidisc ZrO? Extra Translucent are excellently suited to the production of monolithic fully anatomic and partially or fully veneered crowns and bridges with up to 16 units individual abutments for anterior and side teeth on abutment teeth and implants What makes this product so special is its well-balanced relationship between high transparency and flexural strength. This indicates it for an especially wide range of indications.Material: Zirconium dioxide type II, class 5 according to DIN EN ISO 6872 Flexural strength >, 1,150 MPa Exceptional transparency of 45 % Thin wall thickness in the anterior tooth range of 0.4 mm and in the side tooth range of 0.6 mm for individual crowns Precise margins and edges because of a highly condensed material Can be veneered with close to every commercially available ceramic material which is adjusted to the CTE 10 · 10-6 K-1 of ZrO? Batch-independent color accuracy Homogeneous colorization Reproducible colors Biocompatible

priti®multidisc ZrO2 multicolor Extra Translucent, 98 x 25, Color A light

There is a new zirconium dioxide for everyone!priti®multidisc ZrO? multicolor Extra Translucent with a translucence of 45 % and flexural strength >, 1,150 MPa. A cleverly devised zirconium dioxide concept which is an outstanding choice for almost every user. It makes working matchlessly easy. Beautiful &, strong! Real aesthetics - one fits all! Indications: priti®multidisc ZrO? Extra Translucent are excellently suited to the production of monolithic fully anatomic and partially or fully veneered crowns and bridges with up to 16 units individual abutments for anterior and side teeth on abutment teeth and implants What makes this product so special is its well-balanced relationship between high transparency and flexural strength. This indicates it for an especially wide range of indications.Material: Zirconium dioxide type II, class 5 according to DIN EN ISO 6872 Flexural strength >, 1,150 MPa Exceptional transparency of 45 % Thin wall thickness in the anterior tooth range of 0.4 mm and in the side tooth range of 0.6 mm for individual crowns Precise margins and edges because of a highly condensed material Can be veneered with close to every commercially available ceramic material which is adjusted to the CTE 10 · 10-6 K-1 of ZrO? Batch-independent color accuracy Homogeneous colorization Reproducible colors Biocompatible

priti®multidisc ZrO2 multicolor High Translucent, 98x 18, Colour A light

Cubic zirconium, with a translucency of 49 %. Indications: Highly aesthetic monolithic, fully anatomical crowns, partial crowns and bridges with up to 3-units, inlays, onlays and veneers Highly recommended for partially or fully veneered highly aesthetic work Your benefits: highly aesthetic quick easy reproducible Suitable for: open milling system with a blank holder for round blanks with a diameter of 98.5 mm Material: Zirconium type II, class 4 according to DIN EN ISO 6872 Good flexural strength of >, 650 MPa Very high translucency of 49 %, comparable with lithium disilicate Superior aesthetics Very good resistance to aging Thin wall thicknesses for single crowns in the anterior tooth area 0.4 mm and in the posterior tooth area 0.6 mm Biocompatible

Advantages

Properties

Description

Dental technology (english)